Author:Jinli Time:2021-06-09 13:35 Browse(917)
K4388
Introduction: jx-1800bm-62 series strippable ink is specially designed and developed for OGS process. It has high temperature resistance, cutting resistance, ultrasonic resistance, grinding resistance and secondary strengthening hydrofluoric acid resistance.

Supply touch screen protection glue

after use, it can be stripped easily.
no residual glue is left and can be sprayed.
characteristics: & 8 E0 e S9 d%~Color / state blue.
viscosity 400 ~ 600ps, curing condition 150DEG. C x 30min. Hydrofluoric acid (30% HF) resistant for 60 minutes, high temperature (180-250 ℃) resistant for 1-3 hours. Exfoliative ITO glass: exfoliative clean, no foggy residue/U! D $~ - V9 G6 Q9 H5N usage: according to the film thickness setting, the peeling property will be different, Please set the film thickness in the range of 20-30 μ M.
screen setting: 100-150 mesh, emulsion thickness: 30 μ m, Teflon printing setting: scraper hardness: 60-70 ° printing angle: 50-70 ° speed: 20-40cm / sec hardening condition setting: temperature setting: 150 ℃ Time setting: 30 minutes, due to different hardening furnace, the temperature setting is also different.
so please confirm the temperature setting.
pay attention to the cleaning method after use: cleaning screen, container: a small amount of mixed toluene, xylene and other esterification solvent is the best cleaning method.
storage and storage temperature: below 25 ℃, storage life: 6 months from the date of manufacture F) |( ^- e2 ?0 `6 `Sales engineering Miss Zhang: 15814407005: n" r: e9 Y0 B  }9 y2 H$ p; t; l8 Z: D$ f9 F. Z( @8 t9 t$ {QQ:27563928066 W2 O7 m+ \; F- M. }6 M0 pLiufuan Ink Technology Co., Ltd( d: c0 G: c; P4 M  S' U) ~9 I) b# s& U* ^" V' D! x+ m3 }3 X.